Products Description
HIPS (modified benzene # HIPS/modified polystyrene)/MC89/Trinseo
Use: food grade - food packaging, plastic toys, household chores
Characteristic remarks: characteristic: high toughness, easy processing, applicable to the application of mixed general grade polystyrene, and meeting the requirements of the Food and Drug Administration
Important parameters: melt flow rate: 3 g/10min Density: 1.04 g/cm3 Notch impact strength: 101 Tensile strength: 22 MPa Elongation at break: 50% Bending strength: 46 MPa Bending modulus: 2034 MPa Vicat softening point: 101 ℃ Hot deformation temperature: 73 ℃
Manufacturer: Trinseo
Model | MC89 |
Brand Name | Trinseo |
Country Of Origin | Fangchenggang,China |
Exterior | ABS clear particles |
| property | value | test method |
Basic performance rating unit test method | Melt flow rate(200℃/5kg) | (4.5g/10min ) | ASTM D-1238g |
Physical performance rating unit test method | Specific gravity | 1.04g/cm | ASTM D-792 |
| Mold shrinkage rate | 0.004-0.007cm/cm | ASTM D-955 |
Mechanical performance rating unit test method | Tensile yield strength | 26MPa | ASTM D-638 |
| Tensile breaking Strength | 26MPa | ASTM D-638 |
| Elongation at break | 50% | ASTM D-638 |
| Bending strength | 40MPa | ASTM D-790 |
| Bending modulus | 2007MPa | ASTM D-790 |
| IZOD notch Impact strength( (23℃ ) | 128J/m | ASTM D-256 |
Thermal performance | Linear expansion coefficient((10-5)) | 7.4cm/cm/℃ | |
| Flame retardant grade((1.5mm) ) | HB | UL 94 |
| Veka softening point | 105℃ | ASTM D-1525 |
| Thermal deformation temperature (1.82MPa without annealing) (1.82MPa after annealing) | | ASTM D-648 |
| | 80℃ | |
| | 92℃ | |